Standards & Properties: Metallurgy of Copper-Base Alloys

2023-01-30 14:32:02 By : Ms. Vicky Lee

By William D. Nielsen, Jr. Western Reserve Manufacturing Co., Inc.

The basic properties of copper alloys are largely influenced by the properties of copper itself. Copper is known to possess certain unique qualities that make it the best engineering material for bearing applications. These are: H26 Aluminium Sheet

Standards & Properties: Metallurgy of Copper-Base Alloys

All of the three qualities above are directly related to the structure and behavior of copper's structure on an atomic scale.

Solid copper can be described as the arrangement of copper atoms in a face-centered-cubic (fcc) configuration. A copper atom is found at each corner and in the center of each face of a cube as depicted in Figure 1. This is the unit cell which is repeated in three dimensional space to make up the crystal structure of the metal.

The atoms are held in place in the structure by the energy of the atomic attractions between them. It is this particular face-centered cubic arrangement of the atoms that gives copper its high ductility and toughness. All metals deform by means of a mechanism called slip. When slip occurs, a force on the metal causes the atoms to slide past one another in groups. In the copper fcc structure this movement occurs preferentially in any or all of three directions along a specific geometric plane of atoms within the lattice, as shown in Figure 2.

Copper's combination of electronic and crystalographic structures imparts its excellent resistance to corrosion. The free electron cloud is readily available to form coherent films on the metal surface that protect the lattice from further corrosion.

The fcc structure which generates the slip planes imparts another characteristic to these very planes. The atoms on the slip planes are packed as closely together as is possible in any metal system (Figure 2). This efficient arrangement of atoms packs the most matter into a given space (as honeybees seem to know when they build honeycombs). It is very difficult for hydrogen ions to find their way through the small spaces between the atoms and cause stress corrosion cracking except in the most aggressive environments.

We have seen how copper, the base metal for cast bronze, when viewed on the atomic scale, imparts the important characteristics for good bearing materials. But bearings are not made of pure copper, but rather from a wide range of alloys of copper which are now available. Each of these alloys improves on the performance of pure copper and further adapts the new material to specific environments. Let us examine some of the more common alloy systems with respect to the metallurgy of the material and its purpose in bearing design.

The bearing grades of cast bronze can be classified metallurgically into three categories:

To understand the performance of different alloys, we must first understand what happens to the basic copper structure when small amounts of alloying metals are added. Reactions occur during the solidification and cooling of alloys from their molten state.

In simple terms, the final arrangement of the alloying metals with respect to the normal fcc copper lattice determines the properties of the alloy material.

Alloying metals find their place in the copper lattice in three basic ways:

Research has resulted in the graphical representation of how simple binary alloy systems react. This representation is called a phase diagram. The phase diagrams of some binary systems relevant to bronze show the behavior of alloying elements that typically results in one of the three cases mentioned previously. The copper-tin equilibrium phase diagram (Figure 3) illustrates Cases (1) and (2).

An example of such a single-phase commerical alloy is alloy C90300, whose properties are compared with copper in the tabulation below.

If the tin content is increased to 11% or more, some of the alpha phase will transform as the metal cools below 400°C. A new phase appears, interspersed throughout the normal fcc alpha crystals. This phase, called delta, can be preserved in the material with fairly rapid cooling (Figure 5).

The delta phase (though still basically fcc) contains much more tin in proportion to copper than is found in the alpha and is very hard and strong but lacks much ductility. It appears under best conditions as finely dispersed islands throughout the microstructure of the material. The influence of this second phase on the slip mechanism is dramatic, having the effect of pinning the slip planes after small degrees of motion. But the delta phase also greatly increases the wear resistance of the material, as is indicated by the significant increase in hardness. The popular aluminum bronze alloys (C95400 and C95500) and manganese bronzes (C86300 and C86400) gain their high strength and hardness in a similar fashion, although the actors are different. Nonetheless, the properties are the result of the dispersion of another phase (or phases) in the basic fcc lattice with, in nearly all cases, the dispersed phase being much harder and stronger than the bulk of the surrounding matrix material. These "engineered discontinuities" in the material serve to anchor the slip planes and restrict their motion.

These materials are known as polyphase alloys and are characterized by higher strength, hardness and wear resistance than alpha alloys; but they exhibit much less ductility as shown in the tabulation below. As a result, they are best suited for control surface parts where dimensional integrity is most important and for heavy loads and shockloads under slow speeds, aircraft landing gear bearings, for example.

An additional characteristic of the polyphase alloys is that their properties can vary with temperature to significant degrees compared to the single-phase materials. Such alloys are often heat treatable. Through the manipulation of the microstructure of the alloy as shown on the equilibrium phase diagram by "short circuiting" the equilibrium, certain properties can be obtained which are absent in the as-cast condition.

In any case, polyphase materials which do not have significant amounts of lead should only be used as bearings against steel mating surfaces that have themselves been hardened by heat treatment. In the case of aluminum bronze or manganese bronze applications, it is often recommended that the shaft be chrome plated or made from bi-metal material similar to that used for steel mill rolls.

Today it is possible to produce copper-base material with lead content in excess of 30%, wherein the size of the lead particle is microscopic in scale. On the other hand, if the bearing application indicates larger lead particles are more desirable, it is also possible to produce the alloy in that form.

Lead performs three important bearing functions, all of which serve to protect the shaft and improve the performance of the machinery. Of primary importance is the ability of the lead particles to decrease the coefficient of friction between the bearing and the shaft. The mechanism by which this is accomplished is quite interesting. Lead particles are free to be sheared off the bearing surface by microscopic rough edges on the shaft surface. The steel shaft becomes covered with lead which is gradually redistributed to fill in the low spots on the shaft. Once this has been accomplished, the coefficient of friction rises only slightly again, as indicated in the tabulation below (Reference 4). This same phenomenon has a further advantage in that the temperature developed at the points of contact between the bearing and the mated part is limited by the fusion temperature of lead 327, C). Obviously, this property of the leaded alloys is very valuable in the absence of Lubrication (planned or accidental) or if the operating environment of the machine is itself subject to wide temperature extremes, for example on aircraft or arctic oil field equipment.

The second important function of lead is to absorb dirt which finds its way into the interface, although this problem can be avoided through the design of properly sealed bearings whenever possible.

Third, leaded alloys, having somewhat lower strength than the non-leaded copper-tin alloys, and much lower strength than copper-aluminum or copper-zinc alloys, exhibit high degrees of conformability. That is, the bearing will adjust its shape to allow for poor alignment or for vibration. This characteristic, coupled with those previously described, allows one to say that the leaded alloys will "wear-in" very well, a particularly desirable feature for worm gears, to name one example. Lead-containing bronzes are also readily machinable.

The engineer must remind himself that these alloys are not as strong as nonleaded materials, nor do they exhibit as great a resistance to pounding and subsequent fatigue leading to failure. One comforting consideration, however, is that total failure of the bearing is not likely to destroy the shaft or seize the machine, due to the "softness" of these alloys.

By selecting the proper matrix into which the lead particles will be cast, the engineer can select from a fairly wide range of material strength compatible with moderate to light loads and high speeds, as shown in the tabulation below. Values are for continuous castings less than 3 in. in diameter.

Let us now review the bearing bronze alloy families by means of two tables that compare some of their more important engineering properties. Table 1 summarizes the chemical compositions and application properties. Table 2 indicates the more common uses of these materials and their performance qualities in the application environments in which they find the most use.

All of the alloys shown in the tables are essentially variations of the fundamental materials which have been discussed. In some cases, lead may have been added to improve machinability (C92500 vs. C90700). Perhaps nickel has been added to increase strength or corrosion resistance (C95500 vs. 95400). Manganese and iron content may be varied to stabilize certain structures (C86300 vs. C86400). Zinc may have been substituted for tin for the sake of economy (C90500 vs. C90700). One alloy was created out of the prevailing availability of scrap materials (C93200 from C83600 and C93700) and is now perhaps the most widely used bearing alloy. It is a very good compromise. Nonetheless, each material has a unique set of properties that will best fit some particular appreciation.

A few words about the relative economics of the alloy materials are important. All of the alloy components are subject to the influence of world markets, where their price levels are determined by supply, demand, government controls and speculative interest. Fluctuations in the world market for these components ultimately find their way into the composite metal cost for the alloys and this also influences the scrap value of the material when it is removed from service. Table 3 shows the approximate general relative values of copper and the principal alloying materials, at the time this was written.

The bearing grade alloys of copper are available in many forms produced by various methods of manufacture. Cast production methods are summarized in Table 4.

Casting in sand or chill molds are ideal production methods ideal for very small runs or very small parts and are sometimes mandatory for very large parts such as ship propellers.

All of the alloys discussed are available in these forms, although problems with severe lead segregation may occur as the lead content approaches 16%. A wide range of sizes and intricate shapes can be cast. The red brasses, which are very popular as plumbing hardware materials, are produced by these methods, mainly in the form of valve bodies and fittings.

Again, all subject alloys are readily produced by the centrifugal casting method, with the exception of high-leaded tin bronzes in which the lead content approaches 20%. Lead segregation problems are sensitive to the size of the casting. Very large bushings are manufactured by this method. It is likely that most bushings over 14 in. O.D. and up to about 100 in. O.D. are centrifugal castings. Such castings can be made in lengths that exceed 100 in. Nevertheless, small centrifugal castings are also high-volume items. Many of the larger flanged bearings or gear blanks are manufactured by this method. Though sensitive to production quantity, small runs can be very economical. Stocking distributors maintain inventories of semi-finished centrifugal castings, primarily in standard sizes and especially in alloys C95400 and C93200.

All alloys are available as continuous cast barstock; lead segregation is generally not a problem. It may be necessary to stress relieve certain castings with very thin walls, particuarly if the alloy is C95400, C95500 or C86300, to prevent loss of clearance or tolerance in fabrication and use. A wide size range of solid, tubular and made-to-order cross section barstock is available. Diameters range from less than 0.500 in. up to about 14 in. in O.D., in lengths up to about 13 ft. It is possible to produce very thin-walled bars, at times less than 1/4 in., depending on the O.D. These products are ideally suited for further fabrication using automatic machine tools.

Larger quantities of continuous cast products are considerably more economical, but again stocking distributors absorb a great deal of this burden, particularly where alloys C95400, C93200 and C90300 are concerned.

The wrought phosphor bronze alloys (C51000, C52100, C52400, C54400) are sometimes used in bearing applications. These alloys are also available as continuous castings in the annealed temper. Wrought phosphor bronze is usually limited to about 3 in. O.D. and under. C54400 has the highest available lead content, about 4%. It is not possible to extrude or roll alloys with higher lead content.

The aluminum and manganese bronze alloys also have wrought equivalents. The wrought alloys have very strong mechanical properties, having been severely worked either by extrusion, drawing, rolling or forging and are widely used in aerospace applications. Some of these alloys are used as weldment materials. These alloys are also available in different extruded shapes, though the variety available is quite quantity-dependent. Heat treatment of cast alloys produces mechanical properties similar to the wrought materials, as does the continuous casting of the aluminum bronzes. Generally speaking, large production quantities are required to make the wrought products economical, although stocking distributors have assumed this burden for the end-user of smaller quantities.

Some producers, as well as many stocking distributors and bearing houses carry inventories of standard finished bushings, particularly in alloy C93200. These parts are mass-produced and readily available.

A number of machine shops specialize in bearing production, particularly non-standard designs and critical made-to-order alloys. These shops operate sophisticated machining centers. Using the finest available equipment, they are capable of the highest degree of precision in part production and maintain high standards of material quality control. Such establishments serve those OEM establishments and the maintenance departments of larger corporations who choose not to manufacture their own bearings. They provide economical service and are quite knowledgeable about the technology and sources of bearing grade alloys that will best suit the production of a given bearing.

Metallurgical engineering, though very much a science, is also very much an art. Research, extensive experience and a br/oad understanding of the properties which the alloying elements can impart to the copper base metal are essential to good material design. Of equal importance is an understanding of the economics associated with the materials, part production and the operation of the end-use machinery. The remarkable properties of copper, brass and bronze have benefited industries everywhere through their reliable performance, general availability and economic quality.

Standards & Properties: Metallurgy of Copper-Base Alloys

6061 Aluminium Sheet Copyright © 2023 Copper Development Association Inc. All Rights Reserved.